Waste Water management facility undergoing polyurea coating.
Aliphatic

RubberSource Aliphatic ClearCoat is a high solids, color stable aliphatic polyurea coating. RS Aliphatic ClearCoat may be applied directly to most substrates and may be used as a topcoat for existing epoxy, polyurethane, or polyurea. This coating is extremely color stable and displays excellent UV weathering characteristics. RS Aliphatic ClearCoat may be applied in temperatures as low as 20°F. When fully cured, RS Aliphatic ClearCoat will produce a highly abrasion resistant, high-gloss, smooth finish.
Typical Applications
Any exterior use requiring color stability
Automobile dealership floors
Aircraft hangers
  • Hardness:
    ASTM D2240 50 - 60 Shore D Durometer
  • Tensile:
    ASTM D638 1500 - 2500
  • Elongation:
    ASTM D638 95 -115
  • Tear:
    ASTM D624 365 - 500
  • Abrasion:
    ASTM D4060 15 - 20
  • Gel Time:
    N/A
  • Tack Free:
    ASTM D1640 1.5 - 2 Hours
Advantages
Fast cure, high solids, low VOC’s
High tensile strength
Color stable, excellent UV stability
Adheres well to most substrates
Low odor
Cures as low as 20°F
High gloss finish
USDA, FSIS & CFIA approved
Adds new life to epoxy floors
Conforms to SSPC-Paint 39, Type 2
Chemically Resistant Top Coat

RubberSource 25LC Lock Coat Primer is a solvent borne fluoroelastomer, offering outstanding chemical, temperature and permeation resistance. 25LC is designed to be used as a lock coat after the application of 5XEEHU6RXUFH Fast Set Spray materials and provides superior adhesion for the 40VT Finish Coat.
Typical Applications
Acids
Caustics
Fuels
Aqueous solutions
  • Hardness:
    ASTM D2240 >45 Shore A Durometer
  • Tensile:
    ASTM D638 >1800
  • Elongation:
    ASTM D638 500%
  • Tear:
    N/A
  • Abrasion:
    ASTM D4060 0.0042
  • Gel Time:
    N/A
  • Tack Free:
    N/A
Advantages
Excellent resistance to most harsh chemical environments
Continuous operating temperature from -40°F to +400°F
500% elongation
Very low coating permeability
Will not harden or become brittle
Minimal shrinkage after cure
RubberSource 40VT Finish Coat is a combination of Viton and PTFE, offering outstanding chemical, temperature and permeation resistance. 40VT Finish Coat is designed to be used in combination with LC25 Lock Coat and VersaFlex Fast Set Spray materials. RubberSource 40VT is a heavy solids protective top coating suitable for most service environments. The 40VT system may be applied directly to metal. RubberSource recommends up to a 20 dry mil thickness for containment of harsh chemical exposure.
Typical Applications
Acids
Caustics
Fuels
Aqueous solutions
  • Hardness:
    ASTM D2240 15 - 25 Shore D Durometer
  • Tensile:
    ASTM D638 600 - 900
  • Elongation:
    ASTM D638 235 - 290%
  • Tear:
    ASTM D624 70-125
  • Abrasion:
    ASTM D4060 0.002
  • Gel Time:
    N/A
  • Tack Free:
    30 Minutes
Advantages
Excellent resistance to most harsh chemical environments
Continuous operating temperature from -40°F to +400°F
250% elongation
Very low coating permeability
Excellent weather and UV resistance
Will not harden or become brittle
Minimal shrinkage after cure
Flame Resistant, Class 1

RubberSource RS 55DC FR is a fast set, rapid curing, 100% solids, flexible, two-component polyurea elastomer spray coating developed for applications requiring a flame resistant material. RS 55DC FR is Class 1 flame resistant approved and may be used by itself or in combination with other materials to produce coatings, liners, wearing courses and resilient surfaces on concrete and other substrates. RS 55DC FR produces an extremely tough film at all thicknesses. RS 55DC FR may be applied in all positions and to any properly prepared substrates. RS 55DC FR is inert, it will not hydrolyze, leach, or contaminate other materials, and is bondable and paintable. RS 55DC FR is relatively moisture and temperature insensitive, allowing application in the most problematic ambient conditions.
Typical Applications
Industrial facilities
Parking garage decks
Below grade waterproofing
Above grade waterproofing
Water & waste water treatment
Food processing facilities
Pulp & paper mills
Bottling & canning facilities
Walkways & balconies
Secondary containment
  • Hardness:
    ASTM D2240 35 - 40 Shore D Durometer
  • Tensile:
    ASTM D638 1700 - 2300
  • Elongation:
    ASTM D638 400 - 600
  • Tear:
    ASTM D624 350 - 500
  • Abrasion:
    ASTM D4060 150 - 250
  • Gel Time:
    ASTM D1640 20 - 30 Seconds
  • Tack Free:
    ASTM D1640 4 - 5 Minutes
Advantages
Class 1 Flame Resistant Approved Material
100% solids, no VOC’s
Odorless, no toxic vapors
Tough elastomeric membrane
Excellent thermal stability
Minimal downtime
Low permeance rate
Good resistance to a wide range of chemical attack
USDA approved
Installation temperature range from -40°F to 350°F, dry
RubberSource RS 490 FR is a 100% solids elastomeric polyurea developed for applications such as geotextile lining membranes. RS 490 FR is a Class 1 flame resistant coating developed for applications requiring a flame resistant material and may be applied to concrete and steel substrates. RS 490 FR is a volatile free, odorless system applied with 1:1 mix ratio with plural component spray equipment.
Typical Applications
Waterproofing membranes
Geotextile coatings
Secondary containment
Foam coatings
Flexible membranes
Liners
Crude oil condensate pit liners
Oil production water containments
Typical ambient waste water & hydrogen sulfide exposures
  • Hardness:
    ASTM D2240 70 - 80 Shore A Durometer
  • Tensile:
    ASTM D638 1200 - 1800
  • Elongation:
    ASTM D638 300 - 2350
  • Tear:
    ASTM D624 150 - 300
  • Abrasion:
    ASTM D4060 60 - 100
  • Gel Time:
    ASTM D1640 35 - 45 Seconds
  • Tack Free:
    ASTM D1640 6 - 9 Minutes
Advantages
Class 1 Flame Resistant Approved Material
100% solids, no VOC’s
1:1 mix ratio by volume
Rapid cure
Immediate return to service
Applied by plural component spray
Odorless
No VOC’s
Low curing stress shrinkage
Operating temperatures -40°F to 350°F
Industrial Polyurea Coatings

Rubber Source RS DM-SS is a fast set, rapid curing, 100% solids, flexible, two-component polyurea elastomer spray coating material. RS DM-SS is used by itself or in combination with other materials to produce coatings, liners, wearing courses, and resilient surfaces on metal and other substrates. RS DM-SSM produces an extremely tough film at all thicknesses. Single or multiple pass applications produce films from 10 mils to 1,000 mils without appreciable sag or runs. RS DM-SS may be applied in all positions and to any properly prepared surface. RS DM-SS is inert, it will not hydrolyze, leach, or contaminates other materials, and is bondable and paintable. RS DM-SS is relatively moisture and temperature insensitive, allowing application in the most problematic ambient conditions.
Typical Applications
Waterproofing membrane
Chemical plants
Food processing facilities
Liners
Metal coatings
Tank linings
  • Hardness:
    ASTM D2240 50 Shore D Durometer
  • Tensile:
    ASTM D638 2000 - 2800
  • Elongation:
    ASTM D638 200 - 250
  • Tear:
    ASTM D624 300 - 450
  • Abrasion:
    ASTM D4060 15 - 30 C-17, ASTM 150-250 H-18
  • Gel Time:
    ASTM D1640 3 - 7 Seconds
  • Tack Free:
    ASTM D1640 8 - 12 Seconds
Advantages
Odorless, no VOC’s
1:1 mix ratio by volume
Fast return to service
Rapid gel time
Installation temperature range from -40°F to 300°F
Exposure temperatures -40°F to 350°F, dry
RubberSource RS 440 is a fast set, rapid curing, 100% solids, flexible, two-component abrasion resistant polyurea elastomer spray coating material. RS 440 may be used by itself or in combination with other materials to produce coatings, liners, wearing courses, resilient surfaces on metal and other substrates. Its extremely fast gel time makes it suitable for applications down to -40°F without special conditioning of the component resins and isocyanates. RS 440 produces an extremely tough film at varying thicknesses using a multiple pass technique. RS 440 may be applied in all positions and to any properly prepared, sound substrate. RS 440 is inert, it will not hydrolyze, leach, or contaminate other materials, and is bondable and paintable. RS 440 is relatively moisture and temperature insensitive, allowing application in the most problematic ambient conditions.
Typical Applications
Abrasion resistant steel liners
Metal parts
Tank lining
  • Hardness:
    ASTM D2240 50 Shore D Durometer
  • Tensile:
    ASTM D638 2500 - 3000
  • Elongation:
    ASTM D638 400 - 500%
  • Tear:
    ASTM D624 400 - 500
  • Abrasion:
    ASTM D4060 80 - 100
  • Gel Time:
    ASTM D1640 6 - 10 Seconds
  • Tack Free:
    ASTM D1640 12 - 15 Seconds
Advantages
High abrasion resistance
100% solids, no VOC's
1:1 mix ratio by volume
Rapid cure
Fast return to service
Applied by plural component spray
Odorless
Exposure range from -40°F to 300°F, dry
USDA approved
Primer Systems

RubberSource RS30 is a two-component isocyanate and resin blend primer for use on a variety of substrates. RS30 may be diluted to reduce viscosity. RS30 has a working time of 45 minutes. Ponding on the surfaces is to be avoided
RubberSource RS-1 is a specially formulated, low solids, single component primer designed for steel and metal. Its low viscosity contributes to ease of application and adheres well for top coating with RubberSource polyurea products.
Repair Products

RubberSource HM45 is a hand mixable, self-leveling, 100% solids, flexible, twocomponent polyurea and ambient temperature cured material. Designed for small coating applications, slab stabilization, and small patching where mixing by hand or pumping through non-heated plural component equipment is desirable.
Typical Applications
Small repairs on existing polyurea-rips & tears
Slab stabilization
Industrial facilities
Manufacturing facilities
Water & waste water treatment
Food processing facilities
  • Hardness:
    ASTM D2240 45+ Shore D Durometer
  • Tensile:
    ASTM D638 1400 - 1600
  • Elongation:
    ASTM D638 300 - 450
  • Tear:
    ASTM D624 300 - 360
  • Abrasion:
    N/A
  • Gel Time:
    N/A
  • Tack Free:
    45 Minutes
Advantages
100% solids, no VOC’s
Flexible, 450 – 500% elongation
Remains flexible in cold temperatures
Return project to service in 3 hours
Cures from -40°F to 130°F
Odorless, no toxic vapors
Hand mixable and brushable
RubberSource Quick Mender® L.O. is a specially formulated polymer rapid repair product. In its basic low viscosity formulation, Quick Mender® L.O. may be used in a variety of unique applications to repair concrete substrates.
Typical Applications
Repairing spalls and cracks in traffic areas
Restoring integrity to dusted concrete
Filling bug-holes on horizontal surfaces
Repairing horizontal surfaces of concrete and masonry
Bridge deck repairs
Below grade repairs
Spalled control joints
Freezer applications
Polishing concrete floors
  • Hardness:
    ASTM D2240 65 - 75 Shore D Durometer
  • Tensile:
    ASTM D638 2300 - 3000
  • Elongation:
    ASTM D638 1 - 2
  • Tear:
    ASTM D624 260 - 340
  • Abrasion:
    ASTM D4060 250 - 300
  • Gel Time:
    N/A
  • Tack Free:
    ASTM D1640 15 - 20 Minutes
Advantages
Low Odor & VOC’s
Low viscosity in neat configuration will penetrate concrete for permanent bond
Fast return to service in 30 minutes
Can cure in -30°F. Cure time will be extended at lower temperatures
Mix with dry industrial quartz to produce a durable polymer concrete
May be mixed with silica flour, fumed silica, and cabosil
Self-leveling
May be feather edged
Minimal surface preparation required
Good chemical resistance
Secondary Containment

Solvents

RS-TackCoat is a brush or spray applied product used for “waking up” existing polyurea, plastics or synthetic rubber material to accept a new coat of polyurea. Especially useful for the tie-in coat on extended or delayed jobs. Simply apply a light coat to the surface of existing polyurea or plastic and allow to flash off. Top coat with next layer of polyurea within 1 hour. Eliminates the need for hand sanding.
RubberSource VersaFlush is a unique flushing solvent to be used to flush and remove the components of a polyurea or polyurethane plural component system from application equipment. RSVersaFlush replaces other solvents such as DOP, DINP, methylene chloride, acetone, MEK, and 1,1,1 trichloroethane. RS-VersaFlush may be used for extended periods in application equipment and may reduce disposal costs.
RubberSource D-Solve is a water soluble, organic solvent containing no aromatics or petroleum distillates. D-Solve is designed to provide maximum stripping effectiveness while incorporating a high flash point and low toxicity. D-Solve replaces most industrial solvents such as chlorinated hydrocarbons (methylene chloride, carbon tetrachloride and 1,1,1 trichlorethane) when used on cured polymers.